Influence of Pd Thickness on Micro Void Formation of Solder Joints in ENEPIG Surface Finish
Published: |
December 13, 2012 |
Author: |
Dong-Won Shin, Jin-Woo Heo, Yeonseop Yu, Jong-Soo Yoo, Pyoung-Woo Cheon, Seon-Hee Lee |
Abstract: |
First published in the 2012 IPC APEX EXPO technical conference proceedings. We investigated the micro-void formation of solder joints after reliability tests such as preconditioning (precon) and thermal cycle (TC) by varying the thickness of Palladium (Pd) in Electroless Nickel / Electroless Palladium / Immersion Gold (ENEPIG) surface finish. We used lead-free solder of Sn-1.2Ag-0.5Cu-Ni (LF35). We found multiple micro-voids of less than 10 µm line up within or above the intermetallic compound (IMC) layer. The number of micro-voids increased with the palladium (Pd) layer thickness. Our results revealed that the micro-void formation should be related to (Pd, Ni)Sn4 phase resulted from thick Pd layer. We propose that micro-voids may form due to either entrapping of volatile gas by (Pd, Ni)Sn4 or creeping of (Pd, Ni)Sn4.... |
|
Company Information:
More articles from Samsung Electro-Mechanics »
- Dec 16, 2021 - Package-on-Package (PoP) for Advanced PCB Manufacturing Process
- See all SMT / PCB technical articles from Samsung Electro-Mechanics »
More SMT / PCB assembly technical articles »
- Apr 11, 2022 - iNEMI Webinar 07.07.2021 - PCB Cleaning | ZESTRON Americas
- Jan 28, 2022 - Open Radio Unit White Box 5G | Whizz Systems
- Nov 10, 2021 - Understanding the Cleaning Process for Automatic Stencil Printers | ITW EAE
- Oct 20, 2021 - PCB Surface Finishes & The Cleaning Process - A Compatibility Study | ZESTRON Americas
- Oct 06, 2021 - Cleaning Before Conformal Coating | ZESTRON Americas
- Browse Technical Library »
Influence of Pd Thickness on Micro Void Formation of Solder Joints in ENEPIG Surface Finish article has been viewed 507 times