Corrosion Analysis
Published: |
June 3, 2019 |
Author: |
ACI Technologies, Inc. |
Abstract: |
ACI Technologies was pleased to assist a customer by conducting elemental analysis on several assemblies displaying severe corrosion. Several board assemblies had failed in the field and exhibited areas of corrosion in close proximity to onboard components. The most common source of corrosion on electronic assemblies is residual flux. Fluxes are specific chemistries applied during the soldering process which improve the wetting of the solder to both the pad and component when forming the solder joint. They can be highly reactive chemicals that, if left on the assemblies, can lead to corrosion, electrical degradation, and decreased reliability. In the presence of moisture and electrical bias, flux residue can enable dendritic growth as a result of electrochemical migration (ECM).... |
You must be a registered user to talk back to us. |
Company Information:
More articles from ACI Technologies, Inc. »
- Dec 07, 2020 - A Non-destructive Approach to Identify Intermittent Failure Locations on Printed Circuit Cards (PCC) that have been Temperature Cycle Tested
- Nov 09, 2020 - Ball Grid Array (BGA) Voiding Affecting Functionality
- Sep 02, 2020 - Reworking ALD Coatings
- Aug 05, 2020 - ALD of Alumina Ceramic Films for Hermetic Protection
- Jul 01, 2020 - Lead-Free Risk Mitigation -- A Case Study
- See all SMT / PCB technical articles from ACI Technologies, Inc. »
More SMT / PCB assembly technical articles »
- Apr 11, 2022 - iNEMI Webinar 07.07.2021 - PCB Cleaning | ZESTRON Americas
- Jan 28, 2022 - Open Radio Unit White Box 5G | Whizz Systems
- Nov 10, 2021 - Understanding the Cleaning Process for Automatic Stencil Printers | ITW EAE
- Oct 20, 2021 - PCB Surface Finishes & The Cleaning Process - A Compatibility Study | ZESTRON Americas
- Oct 06, 2021 - Cleaning Before Conformal Coating | ZESTRON Americas
- Browse Technical Library »
Corrosion Analysis article has been viewed 502 times